• Prevents non-precious metal alloys from oxidizing
during heat treatment.
• No time-consuming removing of the oxide after
soldering, high luster is maintained and thus
considerable time is saved.
• Perfectly suitable for the use as antiflux.
• Does not contain any flux and is therefore suitable
for ceramic work in all furnaces. |
 |
 |
 |
|
Brush Oxide-Stop onto polished areas of non-precious
structures. |
Oxide-Stop macro avoids oxidation during soldering with
a flame in an efficient manner. |
Remove Oxide-Stop macro with abrasive beads at a
pressure of max. 3 bar. Short polishing is sufficient to
restore mirror-like high lustre. |
 |
 |
 |
|
Brush Oxide-Stop macro onto the CoCr areas to be
protected. Allow to dry for a short time. |
Soldering is carried out in the usual way. Oxide-Stop
macro avoids the formation of an oxide layer. |
Remove Oxide-Stop macro with abrasive beads and polish
shortly. Only unprotected areas have oxidized. |
|
|
Oxide-Stop Silver Palladium
|
|
Prevents oxidation while soldering or firing silver
palladium alloys |
 |
 |
 |
|
Apply a thin coat of Oxide-Stop silver-palladium onto
the areas to be protected and let it dry. A white
protective layer is formed. |
Oxide-Stop silver-palladium avoids the oxidation of the
soldering object while soldered with a flame or in a
furnace. |
Remove Oxide-Stop with the sandblasting unit, in the
ultrasonic unit or with a pickling agent. Re-polishing of
the protected areas is reduced to a minimum degree. |